Spec No. :JEFL243B-9102E-01 P3/10
MURATA MFG.CO.,LTD
Reference Only
8．Q200 Requirement
8-1. Performance (based on Table 13 for Ferrite EMI SUPPRESSORS/FILTERS)
AEC-Q200 Rev.D issued June 1. 2010
AEC-Q200
Murata Specification / Deviation
No
Stress Test Method
3 High Temperature
Exposure
1000hours at +150 deg C
Set for 24hours at room
temperature, then measured.
Meet Table A after testing.
Table A
4 Temperature Cycling
1000cycles
-55 deg C to +150 deg C
Set for 24hours at room
temperature, then measured.
Meet Table A after testing.
5
Destructive
Physical Analysis
Per EIA469
No electrical tests
Not Applicable
7 Biased Humidity
1000hours at 85 deg C, 85%RH
Apply max rated voltage and
current.
Meet Table A after testing.
Apply rated voltage.
(ref.item 9.2)
8 Operational Life
Apply 150 deg C
1000hours
Set for 24hours at room
temperature, then measured.
Meet Table A after testing.
Apply rated current.
(ref.item 9.2)
9 External Visual
Visual inspection No abnormalities
10 Physical Dimension
Meet ITEM 4
（Style and Dimensions）
No defects
12 Resistance to Solvents
Per MIL-STD-202 Method 215 Not Applicable
13 Mechanical Shock
Per MIL-STD-202 Method 213
Condition F:
1500g’s(14.7N)/0.5ms/
Half sine
Meet Table A after testing.
14 Vibration
5g's(0.049N) for 20 minutes,
12cycles each of 3 oritentations
Test from 10-2000Hz.
12cycles each of 3 orientations
Meet Table A after testing.
15 Resistance to
Soldering Heat
No-heating
Solder temperature
260C+/-5 deg C
Immersion time 10s
Pre-heating：150 to 180C / 90±30s
Meet Table A after testing.
17 ESD
Per AEC-Q200-002
Meet Table A after testing.
ESD Rank: Refer to Item 3. Rating.
18 Solderbility
Per J-STD-002
Method b : Not Applicable
90% of the terminations is to be soldered.
(except partly-exposed wire)
Flux:Ethanol solution of rosin,25(wt)% includes activator
equivalent to 0.06 to 0.10(wt)% chlorine
19 Electrical
Characterization
Measured : Impedance No defects.
20 Flammability
Per UL-94
Not Applicable
21 Board Flex
Epoxy-PCB(1.6mm)
Deflection 2mm(min)
60 sec minimum holding time
Meet Table A after testing.
22 Terminal Strength
Per AEC-Q200-006
A force of 17.7N
for 60sec
No defects
30 Electrical Transient
Conduction
Per ISO-7637-2 Not Applicable
Appearance No damage
Common Mode
Impedance
(%ΔZc)
within ±15%
Insulation
Resistance
(I.R.)
Meet item 3