MIL-LT-3/4-9-FSP

Page 4 SPECIFICATION RT-1171 ISSUE 7
If this document is printed it becomes uncontrolled. Check for the latest revision.
TABLE 1
Tubing Dimensions
As Supplied As Recovered
Inside Diameter Inside Diameter Wall Thickness
Size Minimum Maximum Minimum Maximum Nominal
in.
mm.
in.
mm.
in.
mm.
in.
mm.
in.
mm.
3/64 .046 1.17 .023 0.58 .013 0.33 .019 0.48 .016 0.40
1/16 .063 1.60 .031 0.79 .014 0.35 .020 0.50 .017 0.43
3/32 .093 2.36 .046 1.17 .017 0.43 .023 0.58 .020 0.50
1/8 .125 3.18 .062 1.58 .017 0.43 .023 0.58 .020 0.50
3/16 .187 4.75 .093 2.36 .017 0.43 .023 0.58 .020 0.50
1/4 .250 6.35 .125 3.18 .022 0.56 .028 0.71 .025 0.64
3/8 .375 9.53 .187 4.75 .022 0.56 .028 0.71 .025 0.64
1/2 .500 12.70 .250 6.35 .022 0.56 .028 0.71 .025 0.64
3/4 .750 19.05 .375 9.53 .027 0.68 .033 0.84 .030 0.76
1 1.000 25.40 .500 12.70 .030 0.76 .040 1.01 .035 0.88
1-1/2 1.500 38.10 .750 19.05 .034 0.86 .046 1.17 .040 1.01
2 2.000 50.80 1.000 25.40 .038 0.96 .052 1.32 .045 1.14
3 3.000 76.20 1.500 38.10 .042 1.06 .058 1.47 .050 1.27
4 4.000 101.60 2.000 50.80 .046 1.16 .064 1.63 .055 1.39
TABLE 2
Mandrel Dimensions for Bend Testing
Tubing Size Mandrel Diameter
in.
mm.
3/64 to 1/4 inclusive 5/16 ± 0.002 7.9 ± 0.05
3/8 to 1/2 inclusive 3/8 ± 0.003 9.5 ± 0.08
3/4 to 2 inclusive 7/16 ± 0.004 11.1 ± 0.10
3 to 4 7/8 ± 0.005 22.2 ± 0.13
SPECIFICATION RT-1171 ISSUE 7 Page 5
If this document is printed it becomes uncontrolled. Check with the web for the latest revision.
TABLE 3
Requirements
PROPERTY UNIT REQUIREMENT TEST METHOD
PHYSICAL
Dimensions
Inches/(mm)
In accordance with Table 1
Section 4.3.1
Longitudinal Change Percent +0, -5 ASTM D 2671
Tensile Strength psi/(MPa) 1500 minimum (10.3) Section 4.3.2
Ultimate Elongation Percent 200 minimum ASTM D 2671
Secant Modulus (Expanded) psi/(MPa) 2.5 x 10
4
maximum (172) ASTM D 2671
Concentricity (Expanded) Percent 70 minimum ASTM D 2671
Restricted Shrinkage
30 minutes at 175 ± 2°C
(347 ± 4°F)
Proof Voltage 2000 V/a-c
--- No Cracks ASTM D 2671
Procedure A
Specific Gravity (Recovered) --- 1.35 maximum ASTM D 2671
Low Temperature Flexibility
4 hours at -55 ± 3°C
(-67 ± -5°F)
--- No cracking Section 4.3.3
Table 2
Heat Shock
4 hours at 250 ± 3°C
(482 ± 5°F)
--- No dripping, flowing or cracking ASTM D 2671
Heat Resistance
168 hours at 175 ± 2°C
(347 ± 4°F)
Followed by test for:
Tensile Strength
psi/(MPa)
1500 minimum (10.3)
ASTM D 2671
ASTM D2671
Ultimate Elongation Percent 200 minimum
Color --- MIL-STD-104 MIL-STD-104
Color Stability
24 hours at 175 ± 2°C
(347 ± 4°F)
--- MIL-STD-104
ASTM D 2671
Shore A Hardness 85 ± 5 ASTM D 2240
ELECTRICAL
Dielectric Strength
Volts/mil
(volts/mm)
500 minimum (19,680)
Note 1
ASTM D 2671
Volume Resistivity Ohm-cm 10
14
minimum ASTM D 2671
CHEMICAL
Copper Mirror Corrosion
16 hours at 175 ± 2°C
(347 ± 4°F)
---
Non-Corrosive
ASTM D 2671
Procedure A
Copper Contact Corrosion
16 hours at 175 ± 2°C
(347 ± 4°F)
--- No pitting or blackening of
copper.
ASTM D 2671
Procedure B
Flammability --- 1) No flaming or glowing
longer than 1 minute from
any flame application
2) 25% maximum flag burn
3) No burning of cotton.
Self-extinguishing within 15
seconds, no burning or
charring of indicator
ASTM D 2671
Procedure C
ASTM D 2671
Procedure A
Page 6 SPECIFICATION RT-1171 ISSUE 7
If this document is printed it becomes uncontrolled. Check for the latest revision.
TABLE 3
Requirements
(continued)
PROPERTY UNIT REQUIREMENT TEST METHOD
Chemical (continued)
Fungus Resistance
Followed by tests for:
Tensile Strength
Ultimate Elongation
Dielectric Strength
psi (Mpa)
percent
Volts per mil
(volts per mm)
1500 minimum (10.3)
200 minimum
500 minimum (19,700)
ISO 846
Method B
Section 4.3.2
ASTM D 2671
ASTM D 2671
Water Absorption (Recovered)
24 hours at 23 ± 3°C
(73 ± 5°F)
--- 0.5 maximum ASTM D 2671
Fluid Resistance
24 hours at 23 ± 3°C
(73 ± 5°F) in:
JP-8 Fuel
(Mil-DTL-83133)
Skydrol* 500
Hydraulic Fluid
(MIL-H-5606)
Aviation Gasoline 100/300
Lubricating Oil
(MIL-L-7808)
Lubricating Oil
(MIL-L-23699)
Deicing Fluid
(MIL-A-8243)
5% NaCl
Followed by tests for:
---
---
ASTM D 2671
Dielectric Strength Volts/mil
(volts/mm)
400 minimum (15,760)
Tensile Strength psi (MPa) 1000 minimum (6.9)
*Trademark of the Monsanto Company
NOTE 1: Recover the specimens on metal mandrels for 10 minutes, minimum, at 150 ± 3°C (302 ± 5°F) or until the
tubing is completely shrunk on the mandrels.

MIL-LT-3/4-9-FSP

Mfr. #:
Manufacturer:
Raychem / TE Connectivity
Description:
Heat Shrink Tubing and Sleeves HS-TBG 19.1MM FLT WH PRICE PER FT
Lifecycle:
New from this manufacturer.
Delivery:
DHL FedEx Ups TNT EMS
Payment:
T/T Paypal Visa MoneyGram Western Union