Spec No. JELF243B-9102E-01 P.3 / 9
MURATA MFG.CO., LTD
Reference Only
6. Q200 Requirement
6.1. Performance (based on Table 5 for Magnetics (Inductors / Transformer)
AEC-Q200 Rev.D issued June 1. 2010
AEC-Q200 Murata Specification / Deviation
No Stress Test Method
3
High
Temperature
Exposure
1000hours at 125 deg C
Set for 24hours at room
temperature, then measured.
Meet Table A after testing.
Table A
4
Temperature
Cycling
1000cycles
-40 deg C to +125 deg C
Set for 24hours at room
temperature, then measured.
Meet Table A after testing.
7 Biased Humidity 1000hours at 85 deg C, 85%RH
unpowered.
Meet Table A after testing.
8 Operational Life
pply 125 deg C 1000hours
Set for 24hours at room
temperature, then measured
Meet Table A after testing.
9 External Visual
isual inspection No abnormalities
10 Physical Dimension Meet ITEM 4
(Style and Dimensions)
No defects
12 Resistance
o Solvents
Pe
MIL-STD-202
Method 215
Not Applicable
13 Mechanical Shock Per MIL-STD-202
Method 213
Condition C : 100g’s(0.98N), 6ms,
Half sine, 12.3ft/s
Meet Table A after testing.
14
ibration 5g's (0.049N) for 20 minutes,
12cycles each of 3 oritentations
est from 10-2000Hz.
Meet Table A after testing.
15 Resistance
to Soldering Heat
No-heating
Solder temperature
260C+/-5 deg C
Immersion time 10s
Meet Table A after testing.
Pre-heating 150C +/-10 deg C, 60s to 90s
17 ESD Per AEC-Q200-002 Meet Table A after testing.
ESD Rank: refer to the Item3 (Rating).
18 Solderbility Per J-STD-002 Method b: Not Applicable
90% of the terminations is to be soldered.
19 Electrical
Characterization
Measured: Inductance No defects
20 Flammability Per UL-94 Not Applicable
21 Board Flex Epoxy-PCB (1.6mm)
Deflection 2mm (min)
Holding time 60s
Meet Table B after testing.
Table B
22
erminal Strength Per AEC-Q200-006
force of 17.7N
or 60s
No defects
Appearance No damage
Inductance
(at 100MHz)
Within ±10%
Appearance No damage
DC Resistance
Within ±10%