EMI-DS-FOF-85785 051316
Any information furnished by Laird Technologies, Inc. and its agents is believed to be accurate and reliable. All specications are subject to change without notice. Responsibility for the use and application of
Laird Technologies materials rests with the end user. Laird Technologies makes no warranties as to the tness, merchantability, suitability or non-infringement of any Laird Technologies materials or products for
any specic or general uses. Laird Technologies shall not be liable for incidental or consequential damages of any kind. All Laird Technologies products are sold pursuant to the Laird Technologies’ Terms and
Conditions of sale in effect from time to time, a copy of which will be furnished upon request. © Copyright 2013 Laird Technologies, Inc. All Rights Reserved. Laird, Laird Technologies, the Laird Technologies
Logo, and other marks are trade marks or registered trade marks of Laird Technologies, Inc. or an afliate company thereof. Other product or service names may be the property of third parties. Nothing herein
provides a license under any Laird Technologies or any third party intellectual property rights.
APPLICATION TECHNIQUES
COMPOSITION OF PRODUCT
Conductive layer (metallized fabric)
Adhesive layer (acrylic conductive pressure sensitive adhesive)
Release paper
Item Unit Value Test Method
Thickness mm 0.12 ± 0.02 -
Peel Adhesion Kgf / 25 mm >1.1 PSTC 101*
Shear Adhesion
at R.T. Hrs >72 PSTC 107
#
at 80°C Hrs >5 PSTC 107
#
Tensile Strength Kgf / 25 mm >12
Operation Temperature °C 0-80
Surface Resistivity (Fabric Side)
Ω/□
<0.04 ASTM F390
Z-axial Resistance
Ω
<0.04
Shielding Effectiveness
+
ASTM D4935
at 100 MHz dB 75
at 1GHz dB 80
Package Dimensions M W: 5 mm to 1000 mm
L: Standard Length of 20 M
Shelf Life (Under 23°C/65% R.H.)
One Year
*:Test Method A, dwell time 30 min. #:Contact area 25 mm by 25 mm +:Typical value
1. Bond strength is dependent upon the amount of adhesive-to-surface contact developed.
Firm application pressure develops better adhesive contact and improves bond strength.
2. Toobtainoptimumadhesion,thebondingsurfacesmustbeclean,dryandwellunied.
3. The temperature of tape application is recommended 21°C to 38°C.
4. Not designed for cable wrapping or applications requiring high shear adhesion. Please contact
your Laird Sales representative for a more suitable product.
85785 Nickel/Copper
Fabric Tape