Vibration Test
Capacitance change : Amplitude : 1.5mm
within ±2.5% or ±0.25㎊ whichever is larger From 10㎐ to 55㎐ (return : 1min.)
Tan δ, IR : initial spec.
2hours × 3 direction (x, y, z)
Humidity
Capacitance change :
40±2℃, 90~95%RH, 500+12/-0hrs
within ±5% or ±0.5㎊ whichever is larger
Q: 350 min
IR :
1000Mohm or 50Mohm ⋅ ㎌
Whichever is Smaller
Moisture
Capacitance change : With rated voltage
Resistance
within ±7.5% or ±0.75㎊ whichever is larger 40±2℃, 90~95%RH, 500+12/-0hrs
Q : 200 min
IR :
500Mohm or 25Mohm ⋅ ㎌
Whichever is Smaller
High Temperature
Capacitance change : Wit
of the rated voltage
Resistance
within ±3% or ±0.3㎊ whichever is larger
Max. operating temperature
Q : 350 min 1000+48/-0hrs
IR :
1000Mohm or 50Mohm ⋅ ㎌
Whichever is Smaller
Temperature
Capacitance change : 1 cycle condition
Cycling
within ±2.5% or ±0.25㎊ whichever is larger
Min. operating temperatur
→
25℃
Tan δ, IR : initial spec.
→
Max. operating temperature
→
25℃
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.
200%
Performance Test condition