*3M™ Adhesive 100 is a firm acrylic pressure sensitive adhesive system. It features high ultimate bond strength, very good high temperature
and solvent resistance and very high shear holding power. Bond strength increases substantially with natural aging.
3M™ Adhesive 740 is a medium-firm rubber-resin pressure sensitive adhesive system. It features good holding power and adhesion to a
wide variety of surfaces including many low surface energy plastics such as polyethylene and polypropylene.
3M
™
Double Coated Urethane Foam Tapes
4004 • 4008 • 4016 • 4026 • 4032 • 4052 • 4056 • 4085
Units 4032 4052 4056 4085
Adhesive Type:* 100 100 100 740
Adhesive Carrier:
Polyurethane Foam Polyurethane Foam Polyurethane Foam Polyurethane Foam
Thickness: Nominal inch (mm) 0.031 (0.8) 0.031 (0.8) 0.0625 (1.6) 0.045 (1.2)
Thickness: Tolerance: inch 0.025-0.040 0.025-0.040 0.045-0.080 0.039-0.054
(mm) (0.64-1.02) (0.64-1.02) (1.142-2.03) (1.00-1.45)
Color: Natural Black Black Natural
Release Liner: inch (mm) 0.003 (0.08) 0.003 (0.08) 0.003 (0.08) 0.003 (0.08)
Liner Color: Green Plaid Green Plaid Green Plaid Tan
Approximate Density: lb/ft
3
20 14 11 22
(Foam Only) (kg/m
3
) (320) (225) (175) (352)
Standard Length: yard (meter) 72 (65.8) 72 (65.8) 36 (32.9) 72 (65.8)
Maximum Length: yard (meter) 175 (160) 175 (160) 100 (91) 100 (91)
Available Width: inch (mm) 46 (1168) 46 (1168) 46 (1168) 46 (1168)
Normal Slitting Tolerance: inch (mm) ± 1/32 (± 0.8) ± 1/32 (± 0.8) ± 1/32 (± 0.8) ± 1/32 (± 0.8)
Normal Tensile: psi (kPa) 60 (414) 75 (515) 50 (345) 45 (310)
(“T” Block)
1 in
2
(6.45 cm
2
)
Jaw Speed 2 in/min
(50 mm/min)
Static Shear:
72°F (22°C) gms 2000 1500 1500 1000
120°F (49°C) 1500 750 1000 250
150°F (66°C) 1000 750 750 —
200°F (93°C) 1050 750 750 —
Tensile Strength: psi (kPa) 240 (1655) 225 (1550) 140 (965) 140 (965)
Elongation: % 90 110 100 100
Temperature Resistance:
Short Term (Minutes, Hours) °F (°C) 380 (193) 380 (193) 380 (193) 200 (93)
Long Term (Days, Weeks) °F (°C) 220 (104) 220 (104) 220 (104) 125 (152)
Solvent Resistance: No apparent degradation when exposed to splash
tests of most hydrocarbon solvents.
UV Resistance: No apparent degradation when exposed to 7 days in U.V. chamber.
Cold Flex at -20°F (-30°C): No cracking when flexed around a 1/4 in. (6.4 mm mandrel).
Thermal Conductivity: BTU/hr/°F/ft
2
/ft 0.036 0.036 0.036 0.036
(watt/metre Kelvin) (0.062) (0.062) (0.062) (0.062)
Dielectric Strength: volts/mil 200-300 200-300 200-300 200-300
(volts/0.025 mm) (200-300) (200-300) (200-300) (200-300)
Typical Physical Properties
Note: The following technical information and data should be considered representative
or typical only and should not be used for specification purposes.
3M™ Double Coated Urethane Foam Tape
Measured at various
temperatures and
gram loadings.
(1/2 sq. in. overlap).
Will hold listed
weight for 100 hours.
- 3 -