0805YC392JAT2A Datasheet 12102C153KAT2A, 06035C222MAT4A, 1210YC474MAT2A | P1-P3

032117

X7R Dielectric

General Specifications

X7R formulations are called “temperature stable” ceramics and

fall into EIA Class II materials. X7R is the most popular of these

intermediate dielectric constant materials. Its temperature varia-

tion of capacitance is within ±15% from -55°C to +125°C. This

capacitance change is non-linear.

Capacitance for X7R varies under the influence of electrical op-

erating conditions such as voltage and frequency.

X7R dielectric chip usage covers the broad spectrum of

industrial applications where known changes in capacitance

due to applied voltages are acceptable.

PART NUMBER (see page 2 for complete part number explanation)

% Cap Change

-60 -40

-20 0 20 40 60 80

100

120

140

Temperature °C

X7R Dielectric

Typical Temperature Coefficient

-5

-10

-15

-20

-25

% ⌬ Capacitance

+10

+20

+30

-10

-20

-30

1KHz

10 KHz 100 KHz 1 MHz 10 MHz

Frequency

⌬

Capacitance vs. Frequency

Insulation Resistance (Ohm-Farads)

1,000

10,000

100

120

40 60 80

Temperature °C

Insulation Resistance vs Tempera

100

Impedance, ⍀

100 1000

Frequency, MHz

Variation of Impedance with Cap Va

Impedance vs. Frequency

1,000 pF vs. 10,000 pF - X7R

0805



0.10

0.01

1.00

1,000 pF

10,000 pF

10.00

Impedance, ⍀

110

100 1,000

Frequency, MHz

Variation of Impedance with Chip S

Impedance vs. Frequency

100,000 pF - X7R



0.1

.01

1.0

1206

0805

1210

Impedance, ⍀

110

100 1,000

Frequency, MHz

Variation of Impedance with Chip S

Impedance vs. Frequency

10,000 pF - X7R



0.1

.01

1.0

1206

0805

1210

0805

Size

(L" x W")

Voltage

4V = 4

6.3V = 6

10V = Z

16V = Y

25V = 3

50V = 5

100V = 1

200V = 2

500V = 7

Dielectric

X7R = C

103

Capacitance

Code (In pF)

2 Sig. Digits +

Number of Zeros

Capacitance

Tolerance

J = ± 5%*

K = ±10%

M = ± 20%

*≤1μF only,

contact factory for

additional values

Packaging

2 = 7" Reel

4 = 13" Reel

Contact

Factory For

Multiples

Special

Code

A = Std. Product

Terminations

T = Plated Ni

and Sn

7 = Gold Plated*

Z= FLEXITERM

Failure

Rate

A = Not

Applicable

*Optional termination

**See FLEXITERM

X7R section

NOTE: Contact factory for availability of Termination and Tolerance Options for Specific Part Numbers.

Contact factory for non-specified capacitance values.

032117

X7R Dielectric

Specifications and Test Methods

Parameter/Test X7R Specification Limits Measuring Conditions

Operating Temperature Range -55ºC to +125ºC Temperature Cycle Chamber

Capacitance Within specified tolerance

≤ 10% for ≥ 50V DC rating Freq.: 1.0 kHz ± 10%

Dissipation Factor

≤ 12.5% for 25V DC rating Voltage: 1.0Vrms ± .2V

≤ 12.5% for 25V and 16V DC rating

≤ 12.5% for ≤ 10V DC rating

Insulation Resistance

100,000MΩ or 1000MΩ - μF, Charge device with rated voltage for

whichever is less 120 ± 5 secs @ room temp/humidity

Charge device with 250% of rated voltage for

Dielectric Strength No breakdown or visual defects 1-5 seconds, w/charge and discharge current

limited to 50 mA (max)

Note: Charge device with 150% of rated

voltage for 500V devices.

Appearance No defects Deflection: 2mm

Capacitance Test Time: 30 seconds

Resistance to Variation

≤ ±12%

Flexure Dissipation

Meets Initial Values (As Above)

Stresses Factor

Insulation

≥ Initial Value x 0.3

Resistance

Solderability

≥ 95% of each terminal should be covered Dip device in eutectic solder at 230 ± 5ºC

with fresh solder for 5.0 ± 0.5 seconds

Appearance No defects, <25% leaching of either end terminal

Capacitance

Variation

≤ ±7.5%

Dip device in eutectic solder at 260ºC for 60

Dissipation

Meets Initial Values (As Above)

seconds. Store at room temperature for 24 ± 2

Resistance to

Factor

hours before measuring electrical properties.

Solder Heat

Insulation

Meets Initial Values (As Above)

Resistance

Dielectric

Meets Initial Values (As Above)

Strength

Appearance No visual defects Step 1: -55ºC ± 2º 30 ± 3 minutes

Capacitance

Variation

≤ ±7.5% Step 2: Room Temp ≤ 3 minutes

Dissipation

Meets Initial Values (As Above) Step 3: +125ºC ± 2º 30 ± 3 minutes

Thermal

Factor

Shock

Insulation

Meets Initial Values (As Above) Step 4: Room Temp ≤ 3 minutes

Resistance

Dielectric

Meets Initial Values (As Above)

Repeat for 5 cycles and measure after

Strength 24 ± 2 hours at room temperature

Appearance No visual defects

Capacitance

Variation

≤ ±12.5%

Dissipation

≤ Initial Value x 2.0 (See Above)

Load Life Factor

Insulation

≥ Initial Value x 0.3 (See Above)

Resistance

Dielectric

Meets Initial Values (As Above)

Strength

Appearance No visual defects

Capacitance

Variation

≤ ±12.5%

Load Dissipation

≤ Initial Value x 2.0 (See Above)

Humidity Factor

Insulation

≥ Initial Value x 0.3 (See Above)

Resistance

Dielectric

Meets Initial Values (As Above)

Strength

Charge device with 1.5 rated voltage (≤ 10V) in

test chamber set at 125ºC ± 2ºC

for 1000 hours (+48, -0)

Remove from test chamber and stabilize

at room temperature for 24 ± 2 hours

before measuring.

Store in a test chamber set at 85ºC ± 2ºC/

85% ± 5% relative humidity for 1000 hours

(+48, -0) with rated voltage applied.

Remove from chamber and stabilize at

room temperature and humidity for

24 ± 2 hours before measuring.

1mm/sec

90 mm

032117

X7R Dielectric

Capacitance Range

PREFERRED SIZES ARE SHADED

SIZE 0101* 0201 0402 0603 0805 1206

Soldering Reflow Only Reflow Only Reflow/Wave Reflow/Wave Reflow/Wave Reflow/Wave

Packaging

Paper/Embossed All Paper All Paper All Paper Paper/Embossed Paper/Embossed

(L) Length

mm 0.40 ± 0.02 0.60 ± 0.03 1.00 ± 0.10 1.60 ± 0.15 2.01 ± 0.20 3.20 ± 0.20

(in.) (0.016 ± 0.0008) (0.024 ± 0.001) (0.040 ± 0.004) (0.063 ± 0.006) (0.079 ± 0.008) (0.126 ± 0.008)

(W) Width

mm 0.20 ± 0.02 0.30 ± 0.03 0.50 ± 0.10 0.81 ± 0.15 1.25 ± 0.20 1.60 ± 0.20

(in.) (0.008 ± 0.0008) (0.011 ± 0.001) (0.020 ± 0.004) (0.032 ± 0.006) (0.049 ± 0.008) (0.063 ± 0.008)

(t) Terminal

mm 0.10± 0.04 0.15 ± 0.05 0.25 ± 0.15 0.35 ± 0.15 0.50 ± 0.25 0.50 ± 0.25

(in.) (0.004 ± 0.0016) (0.006 ± 0.002) (0.010 ± 0.006) (0.014 ± 0.006) (0.020 ± 0.010) (0.020 ± 0.010)

WVDC 16 10 16 25 50 6.3 10 16 25 50 6.3 10 16 25 50 100 200 6.3 10 16 25 50 100 200 6.3 10 16 25 50 100 200 500

Cap 100 101 B A A A A C C C G G G

(pF) 150 151 B A A A A C C C G G G

220 221 B A A A A C C C G G G

330 331 B A A A A C C C G G G J J J J J J K

470 471 B A A A A C C C G G G J J J J J J K

680 681 B A A A C C C G G G J J J J J J K

1000 102 B A A A C C C C G G G J J J J J J K

1500 152 B A A A C C C C G G J J J J J J J J J J J J M

2200 222 B A A A C C C C G G J J J J J J J J J J J J M

3300 332 A A A C C C C G G J J J J J J J J J J J J M

4700 472 A A A C C C C G G J J J J J J J J J J J J M

6800 682 A A A C C C C G G J J J J J J J J J J J J P

Cap 0.01 103 A A A C C C C G G G J J J J J J J J J J J J P

(μF) 0.015 153 C C C C G G G J J J J J J J J J J J M P

0.022 223 C C C C G G G J J J J J N J J J J J M X

0.033 333 C C C C G G J J J J J N J J J J J M X

0.047 473 C C C C G G G J J J J J N J J J J J M

0.068 683 C C C C G G G J J J J J N J J J J J P

0.1 104 C C C C G G G G J J J J J N J J J J P P

0.15 154 GGGG JJJNN JJJJQ

0.22 224 C G G J J J J J N N N J J J J Q

0.33 334 JJJJ NNNNN JJMPQ

0.47 474 C J J J J J N N N N N M M M P Q

0.68 684 JJJ NNN MMQQQ

1.0 105 C J J J J N N N N M M Q Q Q

2.2 225 J J J P P P P** Q Q Q Q Q**

4.7 475 PP P QQQQ

10 106 PP QQQ

22 226 QQ

47 476

100 107

WVDC 16 10 16 25 50 6.3 10 16 25 50 6.3 10 16 25 50 100 200 6.3 10 16 25 50 100 200 6.3 10 16 25 50 100 200 500

SIZE 0101 0201 0402 0603 0805 1206

Letter ABCEGJKMNPQXYZ

Max. 0.33 0.22 0.56 0.71 0.90 0.94 1.02 1.27 1.40 1.52 1.80 2.29 2.54 2.79

Thickness (0.013) (0.009) (0.022) (0.028) (0.035) (0.037) (0.040) (0.050) (0.055) (0.060) (0.071) (0.090) (0.100) (0.110)

PAPER

EMBOSSED

NOTE: Contact factory for non-specified capacitance values

*EIA 01005

**Contact Factory for Specifications

PAPER and EMBOSSED available for 01005

P1-P3 P4-P4

0805YC392JAT2A

Mfr. #:

Buy 0805YC392JAT2A

Manufacturer:

N/A

Description:

Multilayer Ceramic Capacitors MLCC - SMD/SMT 16V 3900pF 5%

Lifecycle:

New from this manufacturer.

Delivery:

DHL FedEx Ups TNT EMS

Payment:

T/T Paypal Visa MoneyGram Western Union

0805YC392JAT2A

0805YC392JAT2A

Products related to this Datasheet