12.5 Solder Volume
・ Solder shall be used not to be exceeded the upper limits as shown below.
1/3T≦t≦1/2T
T : thickness of product
Accordingly increasing the solder volume, the mechanical stress to Chip is also increased.
Exceeding solder volume may cause the failure of mechanical or electrical performance.
12.6 Attention regarding P.C.B. bending
The following shall be considered when designing and laying out P.C.B.'s.
(1) P.C.B. shall be designed so that products are not subject to the mechanical stress due to
warping the board.
[Products direction]
Products shall be located in the sideways
direction (Length:a<b) to the mechanical
stress.
(2) Products location on P.C.B. separation
Products (A,B,C,D) shall be located carefully
so that products are not subject to the
mechanical stress due to warping the board.
Because they may be subjected the mechanical
stress in order of A>C>B ≅ D.
12.7 Cleaning Conditions
Products shall be cleaned on the following conditions.
(1) Cleaning temperature shall be limited to 60°C max.(40°C max for IPA)
(2) Ultrasonic cleaning shall comply with the following conditions with avoiding the resonance
phenomenon at the mounted products and P.C.B.
Power : 20 W / l max. Frequency : 28kHz to 40kHz Time : 5 min max.
(3) Cleaner
1. Alcohol type cleaner
Isopropyl alcohol (IPA)
2. Aqueous agent
PINE ALPHA ST-100S
(4) There shall be no residual flux and residual cleaner after cleaning.
In the case of using aqueous agent, products shall be dried completely after rinse with de-ionized
water in order to remove the cleaner.
(5) Other cleaning Please contact us.
12.8 Resin coating
When products are coated with resin, please contact us in advance.
12.9 Handling of a substrate
(1)There is a possibility of chip cracking caused by PCBexpansion/contraction with heat, because stress
on a chip is different depending on PCB material and structure.
When the thermal expansion coefficient greatly differs between the board used for mounting and the chip,
it will cause cracking of the chip due to the thermal expansion and contraction.
The chip is assumed to be mounted on the PCB of glass-epoxy material, and we don't test with other
PCB material which has different thermal expansion coefficient from Glass-epoxy.
When other PCB materials are considered, please be sure to evaluate by yourself.
Recommendable
Upper Limit
t
〈
Poor example
〉
〈
Good example
〉
b
a
Seam
Slit
A
D
B
C
b
a
Length:a
<
b