SPECIFICATION CONTROL DRAWING
Page 2 of 2 J
44/0411
SCD Number
Revision
TEMPERATURE RATING: 135°C
Maximum continuous conductor temperature
VOLTAGE RATING: 600 volts (rms) at sea level
ACCELERATED AGING: 225 ± 2°C for 6 hours
BLOCKING: 150 ± 2°C for 24 hours
COLOR: White preferred
FLAMMABILITY: 30 seconds (maximum); 3 in. (maximum); no aming of facial tissue
HUMIDITY RESISTANCE: Insulation Resistance, 5000 megohms for 1000 ft. (minimum)
IDENTIFICATION AND COLOR STRIPING DURABILITY:
125 cycles (250 strokes) (minimum), 500 g weight
IMMERSION: Diameter increase 5% (maximum); no cracking, no dielectric breakdown.
INSULATION ELONGATION AND TENSILE STRENGTH:
Primary Insulation,
Elongation, 150% (minimum)
Tensile Strength, AWG 26-12, 2500 lbf/in² (minimum)
AWG 10, 2000 lbf/in² (minimum)
INSULATION FLAWS:
Primary Insulation,
Spark Test, 1.5 kV (rms)
Impulse Dielectric Test, 6.0 kV (peak)
Finished Wire,
Spark Test, 3.0 kV (rms) at 3 kHz
Impulse Dielectric Test, 8.0 kV (peak)
INSULATION RESISTANCE: 5000 megohms for 1000 ft. (minimum)
LIFE CYCLE: 200 ± 2°C for 120 hours
LOW TEMPERATURE-COLD BEND: -65 ± 2°C for 4 hours
RADIATION RESISTANCE: 500 megarads
SHRINKAGE: 225 ± 2°C,
AWG 26-12 , 0.125 in. (maximum) in 12 inches
AWG 10 , 0.250 in. (maximum) in 12 inches
SMOKE TEST: 165 ± 2°C, no visible smoke.
SURFACE RESISTANCE: 500 megohms-in. (minimum), both readings
THERMAL SHOCK RESISTANCE: 135 ± 2°C, 0.060 in. (maximum)
VACUUM STABILITY:
Total Mass Loss (TML), 1.00% (maximum)
Volatile Condensable Material (VCM), 0.10% (maximum)
VOLTAGE WITHSTAND (Post Environmental):
2500 volts (rms), 60 Hz, 5 minutes; except for the following
AWG 26-24 Life Cycle only: 600 volts (rms), 60 Hz, 5 minutes
WICKING: 2.25 in. (maximum)
PART NUMBER: The "*" in the part numbers on page 1 shall be replaced by color code designators.
1/ Example: AWG 20, white: 44/0411-20-9
AWG 20, white with black stripe: 44/0411-20-90
1/ See footer section on page 1
WIRE RATINGS AND ADDITIONAL REQUIREMENTS