Dual Lock
TM
Reclosable Fasteners
SJ3540(Type 250) • SJ3541(Type 400) • SJ3542(Type 170)
Typical System
Performance
Physical Properties
and Performance
Characteristics
Note: The following technical information and data is intended as a user guide representing
typical performance and should not be used for specifications.
Unless stated differently, typical performance characteristics were measured under controlled laboratory
conditions of 72°F (22°C) and 50% Relative Humidity to obtain maximum reliability. The user should
evaluate products in the actual application to ensure suitable performance for the intended use.
- 2 -
System Performance
(a)
3M™ Dual Lock™ 3M™ Dual Lock™
Reclosable Fastener Reclosable Fastener 3M™ Scotchmate™
SJ3542 (Type 170) SJ3540 (Type 250) SJ3527 (loop)
engaged to engaged to engaged to
3M™ Dual Lock™ 3M™ Dual Lock™ 3M™ Dual Lock™
Reclosable Fastener Reclosable Fastener Reclosable Fastener
SJ3540 (Type 250) SJ3541 (Type 400) SJ3540 (Type 250)
(b)
TENSILE (Rigid to Rigid Substrates) lbs
F
/sq inch (kNewtons/m
2
) @ 72°F/50% RH
Dynamic Tensile Engagement Strength 15 (103) 40 (276) <1 (<6.9)
Dynamic Tensile Disengagement
(c)
35 (241) 66 (455) 35 (242)
Static Tensile Holding Power Holds minimum 1.1 #/in
2
(77.5 grams/cm
2
)
for indicated time and temperature
100°F/100% RH 20,000 minutes 20,000 minutes 20,000 minutes
120°F 20,000 minutes 20,000 minutes 20,000 minutes
140°F 10,000 minutes 10,000 minutes 3,000 minutes
158°F 1,000 minutes 1,500 minutes 275 minutes
SHEAR (Rigid to Rigid Substrates) lbs
F
/sq inch (kNewtons/m
2
)
Dynamic Shear (1" x 1" overlap)
(c)
16 (110) 43 (298) 124 (855)
Static Shear Holding Power Holds minimum 1.1 #/in
2
(77.5 grams/cm
2
)
for indicated time and temperature
100°F/100% RH 7,200 minutes 10,000 minutes 10,000 minutes
120°F 10,000 minutes 10,000 minutes 10,000 minutes
140°F 45 minutes 10,000 minutes 10,000 minutes
158°F 33 minutes 47 minutes 1,000 minutes
PEEL AND CLEAVAGE
(c)
Pounds/inch width (grams/cm width)
Cleavage Strength (Rigid to Rigid) 17 (3040) 30 (5370) 14 (2500)
Peel Strength (“T” Peel, Flexible to Flexible) 0.7 (125) 1.4 (250) 4.1 (730)
Peel Strength (90° Peel, Flexible to Rigid) 1.8 (322) 5.4 (966) 6.1 (1090)
ENGAGED THICKNESS
(d)
Inches (mm) ± Tolerance
(Nominal without liner) 0.27 (6.8) ± 15% 0.27 (6.8) ± 15% 0.17 (4.4) ± 20%
CLOSURE CYCLE LIFE
(e)
1,000 1,000 50
SHELF LIFE
(f)
18 months 18 months 18 months
Note: Long Term Static Load: Conditions such as temperature variations, engagement area, or prolonged periods of exposure to
environmental factors can affect the closure strength and long term static load performance. After engagement fasteners may slip
or creep in the direction of the static load forces when subjected to static loads at temperatures or weights greater than indicated.
The user is responsible for designing the amount of fastening area based upon the specific conditions for the application. Four
square inches of fastening area per pound of static load is suggested as a starting point for such evaluations.
a) The expected system performance of 3M™ Dual Lock™ Reclosable Fasteners is in approximately the following order of increasing
strength: Dual Lock SJ3542 engaged to Dual Lock SJ3540 < (less than) Dual Lock SJ3542 engaged to Dual Lock SJ3541 ≈ (approximately
equal to) Dual Lock SJ3540 engaged to Dual Lock SJ3540 < Dual Lock SJ3540 engaged to Dual Lock SJ3541. Dual Lock SJ3541
engaged to Dual Lock SJ3541 and Dual Lock SJ3542 engaged to Dual Lock SJ3542 are not recommended combinations.
b) Scotchmate loop engaged to Dual Lock provides increased strength over standard 3M™ Scotchmate Reclosable Fasteners. Due to this
increased strength, extra care should be given to ensure the maximum bond strength is obtained to the substrates being joined. Failure to
obtain bond strengths to the substrate that are sufficiently high may cause the fastener to release from the substrate upon disengagement.
c) Dual Lock SJ3540, SJ3541, SJ3542 and Scotchmate SJ3527 were engaged with firm pressure and disengaged, at the rate of 12 inches
(305 mm) per minute.
d) Engaged thickness will decrease if a load is applied or increase if a separation force is applied.
e) Cycle Life is the number of cycles (openings and closings) that the fastener is subjected to while maintaining 50% or greater of the original
tensile values.
f) Shelf life is from date of manufacture when stored in original packaging at 72°F (22°C) and 50% relative humidity.