RW 2053 Revision 2
Page 1 of 7
Date Printed 2/27/2014
If this document is printed it becomes uncontrolled. Check latest revision in DMTEC /Intranet on the nearest PC
RW 2053 Revision 2
RNF-3000 SLEEVING
SCOPE
Approved Signatories*
This document is electronically reviewed and approved and so no signatures will appear.
RW 2053 Revision 2
Page 2 of 7
Date Printed 2/27/2014
If this document is printed it becomes uncontrolled. Check latest revision in DMTEC /Intranet on the nearest PC
1.
REVISION HISTORY
Revision
Number
Change Request
Date
Incorporated By
0
Formerly RK 6150 Revision 3
1
CRF T1020
CR98-DM-0027
28 August 1997
16 February 1998
C. Woosnam
L. Abrams
2
Via DMTEC
27 February 2014
C. Diss
2.
REQUIREMENTS
2.1
Composition, Appearance and Colour
The sleeving shall be homogeneous and free from pinholes, bubbles, cracks and inclusions. The
colour shall be as specified in the contract or order.
2.2
Dimensions
Size
Inside Diameter as
supplied (min)
mm
Inside Diameter after
recovery (max)
mm
Wall Thickness after
recovery
mm
1.5/0.5
1.5
0.5
0.45 ± 0.10
3/1
3.0
1.0
0.55 ± 0.10
6/2
6.0
2.0
0.65 ± 0.10
9/3
9.0
3.0
0.75 ± 0.12
12/4
12.0
4.0
0.75 ± 0.12
18/6
18.0
6.0
0.85 ± 0.12
24/8
24.0
8.0
1.00 ± 0.18
39/13
39.0
13.0
1.15 ± 0.20
Sleeving of special expanded or recovered dimensions may be supplied as specified in the
contract or order.
2.3
Test Requirements
The test requirements shall be as specified in Table 1.
3.
TEST METHODS
3.1
Unless otherwise specified, tests shall be carried out on specimens of sleeving recovered by
conditioning in a fan assisted air circulating oven at 200 ± 5°C for 4 ± 1 minutes and allowed to
cool in air to ambient temperature. No pre-conditioning period is required prior to testing.
Unless otherwise specified, all tests shall be made under standard ambient conditions according
to IEC Publication 212. In cases of dispute the tests shall be carried out at a temperature of 23 ±
2°C and at 50 ± 5% relative humidity.
RW 2053 Revision 2
Page 3 of 7
Date Printed 2/27/2014
If this document is printed it becomes uncontrolled. Check latest revision in DMTEC /Intranet on the nearest PC
3.
TEST METHODS (Cont’d)
3.2
Dimensions and Longitudinal Change
The test method shall be as specified in ASTM D2671.
The length and inside diameter of three 150mm long specimens of expanded sleeving shall be
measured. The specimens shall be recovered in a fan assisted air circulating oven and the length
and inside diameter of each shall be measured. The longitudinal change shall be expressed as a
percentage of the original length. The minimum and maximum recovered wall thickness shall
be determined.
3.3
Tensile Strength and Ultimate Elongation
The test method shall be as specified in ISO 37.
For sleeving of recovered bore greater than 6mm, five Type 2 dumb-bell specimens shall be
tested. For sleeving of recovered bore less than or equal to 6mm, five tubular specimens 125mm
long shall be tested. Initial jaw separation shall be 50 mm and rate of jaw separation shall be
100 ± 10mm per minute.
The test shall be carried out at a temperature of 23 ± 2°C
3.4
Secant Modulus
The test method shall be as specified in Method A of ASTM D882.
For sleeving of recovered bore greater than 6mm, five strip specimens 150mm long shall be
tested. For sleeving of recovered bore less than or equal to 6mm five tubular specimens 150mm
long shall be tested. Initial jaw separation shall be 100mm and rate of jaw separation 10 ± 1mm
per minute.
The test shall be carried out at a temperature of 23 ± 2°C.
3.5
Specific Gravity
The test method shall be as specified in Method A of ISO 1183.
3.6
Heat Shock
The test method shall be as specified in ASTM D2671.
The specimens shall be conditioned in a fan assisted air circulating oven as specified in
Table 1.
3.7
Heat Ageing
The test method shall be as specified in ISO 188.
Five tensile test specimens prepared as in Clause 3.3 shall be conditioned in a fan assisted air
circulating oven as specified in Table 1. After conditioning the specimens shall be removed
from the oven, allowed to cool naturally to room temperature and tested for Ultimate Elongation
according to clause 3.3.
P1-P3P4-P6P7-P7

RNF-3000-39/13-5-SP

Mfr. #:
Buy RNF-3000-39/13-5-SP
Manufacturer:
TE Connectivity
Description:
Heat Shrink Tubing and Sleeves HS-TBG 39/13MM GR PRICE PER METER
Lifecycle:
New from this manufacturer.
Delivery:
DHL FedEx Ups TNT EMS
Payment:
T/T Paypal Visa MoneyGram Western Union

Products related to this Datasheet