SPEC NO: DSAN8290 REV NO: V.3B DATE: JUL/01/2016 PAGE: 2 OF 6
APPROVED: Wynec CHECKED: Allen Liu DRAWN: W.Q.Zhong ERP: 1101033258
Selection Guide
Absolute Maximum Ratings at TA=25°C
Electrical / Optical Characteristics at TA=25°C
Part No. Emitting Color (Material) Lens Type
Angle [1]
Min. Typ. 2θ1/2
WP7113LVBC/D Blue (InGaN) Water Clear 550 1600
20°
Iv (mcd) [2]
@ 2mA
Symbol Parameter Emitting Color Typ. Max. Units Test Conditions
λpeak Peak Wavelength Blue 465 nm IF=2mA
λD [1] Dominant Wavelength Blue 470 nm IF=2mA
Δλ1/2 Spectral Line Half-width Blue 22 nm IF=2mA
C Capacitance Blue 100 pF VF=0V;f=1MHz
VF [2] Forward Voltage Blue 2.65 3.0 V IF=2mA
IR Reverse Current Blue 50 uA VR = 5V
Min.
2.2
Parameter Values Units
Power dissipation 90 mW
DC Forward Current 30 mA
Peak Forward Current [1] 100 mA
Reverse Voltage 5 V
Operating/Storage Temperature -40°C To +85°C
Lead Solder Temperature [2] 260°C For 3 Seconds
Lead Solder Temperature [3] 260°C For 5 Seconds
Electrostatic Discharge Threshold (HBM) 250 V
Notes:
1. θ1/2 is the angle from optical centerline where the luminous intensity is 1/2 of the optical peak value.
2. Luminous intensity / luminous Flux: +/-15%.
3. Luminous intensity value is traceable to CIE127-2007 standards.
Notes:
1. Wavelength: +/-1nm.
2. Forward Voltage: +/-0.1V.
3. Wavelength value is traceable to CIE127-2007 standards.
4. Excess driving current and / or operating temperature higher than recommended conditions may result in severe light degradation or
premature failure.
Notes:
1. 1/10 Duty Cycle, 0.1ms Pulse Width.
2. 2mm below package base.
3. 5mm below package base.
4. Relative humidity levels maintained between 40% and 60% in production area are recommended to avoid the build-up of static
electricity – Ref JEDEC/JESD625-A and JEDEC/J-STD-033.