Multilayer Ceramic Capacitors(High Capacitance)
Item Specifi cation Test Method
Resistance
to Soldering
Heat
Appearance : No mechanical damage
Capacitance change :
Temp. Char. B, X7R, X5R : within ±7.5 %
F, Y5V : within ±20 %
tan
δ
: Initial standard value
IR : Initial standard value
Withstand voltage : No dielectric breakdown or damage
Soldering bath method
Preconditioning : Heat treatment
(
✽
1)
Solder temperature : 270±5 °C
Dipping period : 3.0±0.5 s
Preheat condition :
Order
Temp. (°C)
Size 0805 max.
Size 1206
1
80 to 100 120 to 180s 300 to 360s
2
150 to 200 120 to 180s 300 to 360s
Recovery (Standard condition) : 48±4 h
Solderability More than 95 % of the soldered area of both terminal
electrodes shall be covered with fresh solder.
Soldering bath method
Solder temperature : 230±5 °C
Dipping period : 4±1 s
Solder : H63A (JIS–Z–3282)
Temperature
Cycle
Appearance : No mechanical damage
Capacitance change :
Temp. Char. B, X7R, X5R : within ±7.5 %
F, Y5V : within ±20 %
tan
δ
: Initial standard value
IR : Initial standard value
Withstand voltage : No dielectric breakdown and/or damage
Preconditioning : Heat treatment
(
✽
1)
Step 1: Minimum operating temp. 30±3 min
Step 2: Room temp. 3 min max.
Step 3: Maximum operating temp. 30±3 min
Step 4: Room temp. 3 min max.
Number of cycles : 5 cycles
Recovery(Standard condition) : 48±4 h
Damp Heat
(steady state)
Appearance : No mechanical damage
Capacitance change :
Temp. Char. B, X7R, X5R : within ±20 %
F, Y5V : within ±30 %
tan
δ
: Temp. Char. B, X7R, X5R : 0.25 max.
F, Y5V : 0.3 max.
IR : 50/C (M
액
) min.
Note : 10/C (M
액
) min. for rated vol. DC 10 V max.
C:Nominal cap. in µF
Please see the technical specifi cations for details.
Preconditioning : Heat treatment
(
✽
1)
Temperature : 40±2 °C
Relative humidity : 90 to 95 %
Test period : 500+24/0 h
Recovery(Standard condition) : 48±4 h
Damp Heat
Load
Appearance : No mechanical damage
Capacitance change :
Temp. Char. B, X7R, X5R : within ±20 %
F, Y5V : within ±30 %
tan
δ
: Temp. Char. B, X7R, X5R : 0.25 max.
F, Y5V : 0.3 max.
IR : 25/C (M
액
) min.
Note : 5/C (M
액
) min. for rated vol. DC 10 V max.
C:Nominal cap. in µF
Please see the technical specifi cations for details.
Preconditioning : Voltage treatment
(
✽
2)
Temperature : 40±2 °C
Relative humidity : 90 to 95 %
Applied voltage : Rated voltage
Charge/discharge current : 50 mA max.
Test period : 500+24/0 h
Recovery(Standard condition) : 48±4 h
High
Temperature
Load
Appearance : no mechanical damage
Capacitance change :
Temp. Char. B, X7R, X5R : within ±20 %
F, Y5V : within ±30 %
tan
δ
: Temp. Char. B, X7R, X5R : 0.25 max.
F, Y5V : 0.3 max.
IR : 50/C (M
액
) min.
Note : 10/C (M
액
) min. for rated vol. DC 10 V max.
C:Nominal cap. in µF
Please see the technical specifi cations for details.
Preconditioning : Voltage treatment
(
✽
2)
Temperature : Maximum operation temp. ±3 °C
Applied voltage : (1)Rated volt age
҂
200 %
(2)Rated voltage
҂
150 %
(3)Rated voltage
҂
100 %
Please see the technical specifi cations
for details.
Charge/discharge current : 50 mA max.
Test period : 1000+48/0 h
Recovery (Standard condition) : 48±4 h
(
✽
1) Heat treatment : 1 h of heat treatment at 150+0/–10 °C followed by 48±4 h recovery under standard conditions.
(
✽
2) Voltage treatment : 1 h of voltage treatment under the specifi ed temperature and voltage for testing followed by 48±4 h of recovery under
standard conditions.