PS2815-1,PS2815-4
NOTES ON HANDLING
1. Recommended soldering conditions
(1) Infrared reflow soldering
Peak reflow temperature 260°C or below (package surface temperature)
Time of peak reflow temperature 10 seconds or less
Time of temperature higher than 220°C 60 seconds or less
Time to preheat temperature from 120 to 180°C 120±30 s
Number of reflows Three
Flux Rosin flux containing small amount of chlorine (The flux with a
maximum chlorine content of 0.2 Wt% is recommended.)
120±30 s
(preheating)
220°C
180°C
Package Surface Temperature T (°C)
Time (s)
Recommended Temperature Profile of Infrared Reflow
(heating)
to 10 s
to 60 s
260°C MAX.
120°C
(2) Wave soldering
• Temperature 260°C or below (molten solder temperature)
Time 10 seconds or less
• Preheating conditions 120°C or below (package surface temperature)
Number of times One (Allowed to be dipped in solder including plastic mold portion.)
Flux Rosin flux containing small amount of chlorine (The flux with a maximum chlorine
content of 0.2 Wt% is recommended.)
(3) Soldering by soldering iron
Peak temperature (lead part temperature) 350°C or below
Time (each pins) 3 seconds or less
Flux Rosin flux containing small amount of chlorine (The flux with a
maximum chlorine content of 0.2 Wt% is recommended.)
(a) Soldering of leads should be made at the point 1.5 to 2.0 mm from the root of the lead.
(b) Please be sure that the temperature of the package would not be heated over 100°C.
Data Sheet PN10256EJ04V0DS
10
PS2815-1,PS2815-4
(4) Cautions
• Fluxes
Avoid removing the residual flux with freon-based and chlorine-based cleaning solvent.
2. Cautions regarding noise
Be aware that when voltage is applied suddenly between the photocoupler’s input and output or between
collector-emitters at startup, the output transistor may enter the on state, even if the voltage is within the absolute
maximum ratings.
3. Measurement conditions of current transfer ratios (CTR), which differ according to photocoupler
Check the setting values before use, since the forward current conditions at CTR measurement differ according
to product.
When using products other than at the specified forward current, the characteristics curves may differ from the
standard curves due to CTR value variations or the like. Therefore, check the characteristics under the actual
operating conditions and thoroughly take variations or the like into consideration before use.
USAGE CAUTIONS
1. Protect against static electricity when handling.
2. Avoid storage at a high temperature and high humidity.
Data Sheet PN10256EJ04V0DS
11
PS2815-1,PS2815-4
SPECIFICATION OF VDE MARKS LICENSE DOCUMENT
Parameter Symbol Spec. Unit
Climatic test class (IEC 60068-1/DIN EN 60068-1) 55/100/21
Dielectric strength
maximum operating isolation voltage
Test voltage (partial discharge test, procedure a for type test and random test)
U
pr = 1.5 × UIORM, Pd < 5 pC
U
IORM
Upr
705
1 058
V
peak
Vpeak
Test voltage (partial discharge test, procedure b for all devices)
U
pr = 1.875 × UIORM, Pd < 5 pC
U
pr 1 322 Vpeak
Highest permissible overvoltage UTR 6 000 Vpeak
Degree of pollution (DIN EN 60664-1 VDE0110 Part 1) 2
Comparative tracking index (IEC 60112/DIN EN 60112 (VDE 0303 Part 11)) CTI 175
Material group (DIN EN 60664-1 VDE0110 Part 1) III a
Storage temperature range Tstg –55 to +150 °C
Operating temperature range TA –55 to +100 °C
Isolation resistance, minimum value
V
IO = 500 V dc at TA = 25°C
V
IO = 500 V dc at TA MAX. at least 100°C
Ris MIN.
Ris MIN.
10
12
10
11
Ω
Ω
Safety maximum ratings (maximum permissible in case of fault, see thermal
derating curve)
Package temperature
Current (input current I
F, Psi = 0)
Power (output or total power dissipation)
Isolation resistance
V
IO = 500 V dc at TA = Tsi
Tsi
Isi
Psi
Ris MIN.
150
300
500
10
9
°C
mA
mW
Ω
Data Sheet PN10256EJ04V0DS
12

PS2815-1-F3-A

Mfr. #:
Manufacturer:
Renesas Electronics
Description:
Transistor Output Optocouplers Hi CTR AC Input 1-Ch
Lifecycle:
New from this manufacturer.
Delivery:
DHL FedEx Ups TNT EMS
Payment:
T/T Paypal Visa MoneyGram Western Union