Typical Physical Properties and Performance Characteristics
Note: The following technical information and data should be considered representative or typical only and should
not be used for specification purposes.
3M™ Bumpon™ Resilient Rollstock Series
Property Test Method*** SJ5200 SJ5800 SJ5900 SJ6000 SJ6200
Hardness, Shore M ASTM-D-2240 36 (SJ5216) 72 40 (SJ5916) 72 72
29 (SJ5208) 36 (SJ5908,
SJ5904)
Approximate Density, lb/ft
3
40 80 40 80 80
(g/cm
3
) (0.64) (1.3) (0.64) (1.3) (1.3)
Kinetic Coefficient of Friction* ASTM-D-1894
Stainless Steel * > 1 > 1 > 1 > 1
Glass * > 1 > 1 > 1 > 1
Formica
®
laminate * 0.9 - 1.4 0.8 - 1.4 0.9 - 1.4 0.9 - 1.4
Wood * 0.9 - 1.4 0.8 - 1.4 0.9 - 1.4 0.9 - 1.4
* Two important laws of friction applicable to 3M™ Bumpon™ Resilient Rollstock are: (1) Friction is independent of the area of contact
between solids. (2) Friction is proportional to the load between solid surfaces. Thus, if the load (weight) is doubled, the force required to
cause surface sliding is also doubled. This is expressed mathematically as follows:
Sliding force = (kinetic coefficient of friction) x (weight)
Abrasion Resistance ASTM-C-501 * 1.7 - 1.9 1.8 - 2.0 1.7 - 1.9 1.7 - 1.9
Taber H 18, 1 kg, g/1000 cycles
Tensile, lb/in
2
ASTM-D-412, Die A * 600 120 600 600
(kPa) (4140) (830) (4140) (4140)
Elongation, % ASTM-D-412, Die A * 100 100 100 100
Compression Set, % ASTM-D-1056 8 – 12 – –
(50% deflection) 10 – 14 – –
ASTM-D-395 – 3 – 3 3
(25% deflection) – 4 – 4 4
Dielectric Strength, volts/mil ASTM-D-1000 * 200 140 200 200
Flammability Listing UL Classification * UL94HB UL94HBF UL94HB UL94HB
(except SJ5916)
Stain Resistance** 3M - 24 hrs. @ 158°F against No staining observed
white paint, 7 days exposed to UV
Ozone and Oxygen Resistance** 3M - 30 days @ 50 ppm ozone No visual deterioration
Solvent and Fuel Resistance** 3M - 24 hr. immersion
5% Detergent in water No apparent effect
25% Ammonia in water No apparent effect
Bleach No apparent effect
Hydrochloric Acid (1 normal solution) No apparent effect
Diesel Fuel No apparent effect
Auto Oil No apparent effect
Isopropyl Alcohol Slight effect (swelling)
Heptane Slight effect (swelling)
Toluene (Toluol) Considerable effect (swelling)
Lacquer Thinner Considerable effect (swelling)
Load Tolerance The recommended maximum load which Bumpon Resilient Rollstock series SJ5800, SJ6000
and SJ6200 will support is 100 psi (690 kPa) at 70°F (21°C) to 120°F (49°C).
Environmental Performance Bumpon Resilient Rollstock is intended for interior applications where resilience and all other
physical properties will remain unchanged. When exposed to UV light for extended periods,
some discoloration may occur. Bumpon resilient rollstock may be used outdoors in a protected
area with some discoloration and chalking possible.
* = Not tested for Bumpon SJ5200 Series (soft foam)
** = Reference test for time periods specified only.
Results may vary for different product application conditions.
*** = When ASTM method is listed, data was collected in accordance with ASTM test method.