RECOMMENDED SOLDERING CONDITIONS
This product should be soldered and mounted under the following recommended conditions. For soldering
methods and conditions other than those recommended below, contact your nearby sales office.
Soldering Method Soldering Conditions Condition Symbol
Infrared Reflow Peak temperature (package surface temperature) : 260°C or below
Time at peak temperature : 10 seconds or less
Time at temperature of 220°C or higher : 60 seconds or less
Preheating time at 120 to 180°C : 120±30 seconds
Maximum number of reflow processes : 3 times
Maximum chlorine content of rosin flux (% mass) : 0.2%(Wt.) or below
IR260
VPS Peak temperature (package surface temperature) : 215°C or below
Time at temperature of 200°C or higher : 25 to 40 seconds
Preheating time at 120 to 150°C : 30 to 60 seconds
Maximum number of reflow processes : 3 times
Maximum chlorine content of rosin flux (% mass) : 0.2%(Wt.) or below
VP215
Wave Soldering Peak temperature (molten solder temperature) : 260°C or below
Time at peak temperature : 10 seconds or less
Preheating temperature (package surface temperature) : 120°C or below
Maximum number of flow processes : 1 time
Maximum chlorine content of rosin flux (% mass) : 0.2%(Wt.) or below
WS260
Partial Heating Peak temperature (pin temperature) : 350°C or below
Soldering time (per side of device) : 3 seconds or less
Maximum chlorine content of rosin flux (% mass) : 0.2%(Wt.) or below
HS350
Caution Do not use different soldering methods together (except for partial heating).