VJ....31X RoHS Automotive MLCC
www.vishay.com
Vishay Vitramon
Revision: 29-May-18
1
Document Number: 45226
For technical questions, contact: mlcc@vishay.com
THIS DOCUMENT IS SUBJECT TO CHANGE WITHOUT NOTICE. THE PRODUCTS DESCRIBED HEREIN AND THIS DOCUMENT
ARE SUBJECT TO SPECIFIC DISCLAIMERS, SET FORTH AT www.vishay.com/doc?91000
Surface Mount Multilayer Ceramic Chip Capacitors
for Automotive Applications
FEATURES
• AEC-Q200 qualified with PPAP available
• Available in 0402 to 1812 body size
• High operating temperature
• Wet build process
• Reliable Noble Metal Electrode (NME) system
• Parts compliant with ELV directive
• Material categorization: for definitions of compliance
please see www.vishay.com/doc?99912
For more than 25 years Vishay Vitramon has supported the automotive industry with robust, highly reliable MLCCs that have
made it a leader in this segment. All Vishay Vitramon MLCCs are manufactured in “Precious Metal Technology” (PMT / NME)
and a wet build process. They are qualified according to AEC-Q200 with PPAP available on request. Applications for these
devices include automotive “under the hood”, safety and comfort electronics. Their termination finish is 100 % matte tin plate
finish. A polymer (flexible) termination with 100 % matte tin plate finish is offered for boardflex sensitive applications.
C0G (NP0) DIELECTRIC
GENERAL SPECIFICATION
Note
Electrical characteristics at +25 °C unless otherwise specified
Operating Temperature: -55 °C to +150 °C
(above +125 °C changed characteristics, see 2.2)
Capacitance Range: 1 pF to 22 nF
Voltage Range: 25 V
DC
to 3000 V
DC
Temperature Coefficient of Capacitance (TCC):
0 ppm/°C ± 30 ppm/°C from -55 °C to +125 °C
Dissipation Factor (DF):
0.1 % maximum at 1.0 V
RMS
and
1 MHz for values 1000 pF
0.1 % maximum at 1.0 V
RMS
and
1 kHz for values > 1000 pF
Insulating Resistance:
at +25 °C 100 000 M min. or 1000 F whichever is less
at +125 °C 10 000 M min. or 100 F whichever is less
Aging: 0 % maximum per decade
Dielectric Strength Test:
performed per method 103 of EIA 198-2-E.
Applied test voltages
250 V
DC
-rated: 250 % of rated voltage
500 V
DC
-rated: 200 % of rated voltage
630 V
DC
, 1000 V
DC
-rated: 150 % of rated voltage
3000 V
DC
-rated: 120 % of rated voltage
X7R, X8R DIELECTRIC
GENERAL SPECIFICATION
Note
Electrical characteristics at +25 °C unless otherwise specified
Operating Temperature: -55 °C to +150 °C
(X7R above +125 °C changed characteristics, see 2.2)
Capacitance Range: 120 pF to 1.0 μF
Voltage Range: 16 V
DC
to 1000 V
DC
Temperature Coefficient of Capacitance (TCC):
X7R: ± 15 % from -55 °C to +125 °C, with 0 V
DC
applied
X8R: ± 15 % from -55 °C to +150 °C, with 0 V
DC
applied
Dissipation Factor (DF):
16 V, 25 V ratings: 3.5 % maximum at 1.0 V
RMS
and 1 kHz
> 25 V ratings: 2.5 % maximum at 1.0 V
RMS
and 1 kHz
Insulating Resistance:
at +25 °C 100 000 M min. or 1000 F whichever is less
at +125 °C 10 000 M min. or 100 F whichever is less
Aging Rate: 1 % maximum per decade
Dielectric Strength Test:
performed per method 103 of EIA 198-2-E.
Applied test voltages
250 V
DC
-rated: 250 % of rated voltage
500 V
DC
-rated: min. 150 % of rated voltage
630 V
DC
, 1000 V
DC
-rated: min. 120 % of rated voltage